Jim's Articles

Microscopy and elemental mapping laboratories with MicroVision Laboratories

Microscopy lab and elemental mapping services in Chelmsford, MA? Approach: MicroVision Labs’ staff consulted with the client, and determined that, unfortunately, there could be a number of potential sources of a white material. Even before the bottle with the suspended material arrived, it was determined that there was less than 50 mL of water remaining, and likely less than a gram of material suspended in the water. The client was aware that this material could represent precipitated minerals from the source water, a polymer residue from the bottles, some form of biological tissue that might have formed despite sterilization procedures, or could very well represent some completely unforeseen foreign material. The issue facing the client is how to have the material tested, as most tests that they might request for one or the other of these known potential sources would destroy or alter the sample. Choosing a test was therefore something of a gamble, because if they tested for calcium (mineral precipitate) and it came up negative – that didn’t actually tell them what the powder was, just that it didn’t have any calcium. Based on this conversation, the non-destructive, specialized testing at MicroVision Laboratories was chosen as the best choice.

Energy Dispersive X-Ray Spectroscopy (EDS): While in a Scanning Electron Microscope (SEM), samples are exposed to high energy electrons in a vacuum, which generates X-rays through secondary electron transitions. Variations in electron configuration specific to each element generate different energy electrons, and thus different signature energy peaks, indicating which elements are present in the sample. Analysis is performed only on areas which are exposed to the electron beam, facilitating precise control of the analyzed area. This means the composition of very small areas or particles in a sample can be taken. Since EDS is performed in the SEM chamber, a quick and easy interrogation of the surface materials as viewed on the SEM is possible. This can be expanded to include the entire sample, please see our Elemental Mapping page. Additionally, relative amount of the elements present can be calculated, generating composition percentages.

What is your standard turnaround time (TAT) and can it be expedited? Our standard TAT is 5 to 10 business days. We can provide faster TATs on request with the following surcharges: – Same day to 24 hour rush is 100% surcharge – 2 day rush is 75% surcharge – 3 day rush is 50% surcharge – 4 day rush is 25% surcharge Rush requests must have prior approval otherwise we cannot guarantee turnaround times. See additional info at info on elemental labs.

The desired chip packages were sectioned from the larger board, and placed in an epoxy mounting cup. The epoxy was mixed and allowed to harden. The resulting epoxy puck was cross sectioned and polished. The epoxy mounting and cross sectioning process gave precise, perfectly preserved cross sectional surfaces through the desired components and their solder bonds.

MicroVision Laboratories, Inc. has been providing extensive expertise in micro-analytical techniques (FE-SEM, SEM, EDS, XRF, FTIR testing, PLM, X-Ray Imaging, DIC) and sample preparation since 2003. Our cutting edge, high-performance equipment combined with our solutions-focused customer service provide critical solutions for clients hailing from a broad range of industries ranging from medical to semiconductor, and from environmental to textile.

Examining the sample with a polarized light microscope (PLM), it was darker and coarser than expected for a mold sample. The dust appeared to be a closed cell, synthetic blown foam material, and all from the same source. The black color was likely due to pigment particles added to color the foam. Fourier Transform Infra-Red spectroscopy was performed on the foam particles. The spectrum showed a mixture of spectral features, associated with vinyl acetates, polyurethane, and cellulose or other sugar-like polymers. Based on these features, a common urethane acetate foam was determined as the likely source material. Read a few extra details at https://microvisionlabs.com/.